Head tracking servo method for magnetic tape recording device

ABSTRACT

The magnetic tape device includes a magnetic tape and a TMR head (servo head), in which the magnetic tape includes a non-magnetic support, and a magnetic layer including ferromagnetic powder and a binding agent on the non-magnetic support, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, an intensity ratio of a peak intensity Int(110) of a diffraction peak of a (110) plane with respect to a peak intensity Int(114) of a diffraction peak of a (114) plane of a hexagonal ferrite crystal structure obtained by an X-ray diffraction analysis of the magnetic layer by using an In-Plane method is 0.5 to 4.0, and a vertical direction squareness ratio of the magnetic tape is 0.65 to 1.00.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority under 35 U.S.C 119 to Japanese Patent Application No. 2017-065694 filed on Mar. 29, 2017. The above application is hereby expressly incorporated by reference, in its entirety, into the present application.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a magnetic tape device and a head tracking servo method.

2. Description of the Related Art

Magnetic recording is used as a method of recording information on a recording medium. In the magnetic recording, information is recorded on a magnetic recording medium as a magnetized pattern. Information recorded on a magnetic recording medium is reproduced by reading a magnetic signal obtained from the magnetized pattern by a magnetic head. As a magnetic head used for such reproducing, various magnetic heads have been proposed (for example, see JP2004-185676A).

SUMMARY OF THE INVENTION

An increase in recording capacity (high capacity) of a magnetic recording medium is required in accordance with a great increase in information content in recent years. As means for realizing high capacity, a technology of increasing a recording density of a magnetic recording medium is used. However, as the recording density increases, a magnetic signal (specifically, a leakage magnetic field) obtained from a magnetic layer tends to become weak. Accordingly, it is desired that a high-sensitivity magnetic head capable of reading a weak signal with excellent sensitivity is used as a reproducing head. Regarding the sensitivity of the magnetic head, it is said that a magnetoresistive (MR) head using a magnetoresistance effect as an operating principle has excellent sensitivity, compared to an inductive head used in the related art.

As the MR head, an anisotropic magnetoresistive (AMR) head and a giant magnetoresistive (GMR) head are known as disclosed in a paragraph 0003 of JP2004-185676A. The GMR head is an MR head having excellent sensitivity than that of the AMR head. In addition, a tunnel magnetoresistive (TMR) head disclosed in a paragraph 0004 and the like of JP2004-185676A is an MR head having a high possibility of realizing higher sensitivity.

Meanwhile, a recording and reproducing system of the magnetic recording is broadly divided into a levitation type and a sliding type. A magnetic recording medium in which information is recorded by the magnetic recording is broadly divided into a magnetic disk and a magnetic tape. Hereinafter, a drive including a magnetic disk as a magnetic recording medium is referred to as a “magnetic disk device” and a drive including a magnetic tape as a magnetic recording medium is referred to as a “magnetic tape device”.

The magnetic disk device is generally called a hard disk drive (HDD) and a levitation type recording and reproducing system is used. In the magnetic disk device, a shape of a surface of a magnetic head slider facing a magnetic disk and a head suspension assembly that supports the magnetic head slider are designed so that a predetermined interval between a magnetic disk and a magnetic head can be maintained with air flow at the time of rotation of the magnetic disk. In such a magnetic disk device, information is recorded and reproduced in a state where the magnetic disk and the magnetic head do not come into contact with each other. The recording and reproducing system described above is the levitation type. On the other hand, a sliding type recording and reproducing system is used in the magnetic tape device. In the magnetic tape device, a surface of a magnetic layer of a magnetic tape and a magnetic head come into contact with each other and slide on each other, at the time of the recording and reproducing information.

JP2004-185676A proposes usage of the TMR head as a reproducing head for reproducing information in the magnetic disk device. On the other hand, the usage of the TMR head as a reproducing head in the magnetic tape device is currently still in a stage where the future usage thereof is expected, and the usage thereof is not yet practically realized.

However, in the magnetic tape, information is normally recorded on a data band of the magnetic tape. Accordingly, data tracks are formed in the data band. As means for realizing high capacity of the magnetic tape, a technology of disposing the larger amount of data tracks in a width direction of the magnetic tape by narrowing the width of the data track to increase recording density is used. However, in a case where the width of the data track is narrowed and the recording and/or reproduction of information is performed by transporting the magnetic tape in the magnetic tape device, it is difficult that a magnetic head properly follows the data tracks in accordance with the position change of the magnetic tape, and errors may easily occur at the time of recording and/or reproduction. Thus, as means for preventing occurrence of such errors, a method of forming a servo pattern in the magnetic layer and performing head tracking servo has been recently proposed and practically used. In a magnetic servo type head tracking servo among head tracking servos, a servo pattern is formed in a magnetic layer of a magnetic tape, and this servo pattern is read by a servo head to perform head tracking servo. The head tracking servo is to control a position of a magnetic head in the magnetic tape device. The head tracking servo is more specifically performed as follows.

First, a servo head reads a servo pattern to be formed in a magnetic layer (that is, reproduces a servo signal). A position of a magnetic head in a magnetic tape device is controlled in accordance with a value obtained by reading the servo pattern. Accordingly, in a case of transporting the magnetic tape in the magnetic tape device for recording and/or reproducing information, it is possible to increase an accuracy of the magnetic head following the data track, even in a case where the position of the magnetic tape is changed. For example, even in a case where the position of the magnetic tape is changed in the width direction with respect to the magnetic head, in a case of recording and/or reproducing information by transporting the magnetic tape in the magnetic tape device, it is possible to control the position of the magnetic head of the magnetic tape in the width direction in the magnetic tape device, by performing the head tracking servo. By doing so, it is possible to properly record information in the magnetic tape and/or properly reproduce information recorded on the magnetic tape in the magnetic tape device.

The servo pattern is formed by magnetizing a specific position of the magnetic layer. A plurality of regions including a servo pattern (referred to as “servo bands”) are generally present in the magnetic tape capable of performing the head tracking servo along a longitudinal direction. A region interposed between two servo bands is referred to as a data band. The recording of information is performed on the data band and a plurality of data tracks are formed in each data band along the longitudinal direction. In order to realize high capacity of the magnetic tape, it is preferable that the larger number of the data bands which are regions where information is recorded are present in the magnetic layer. As means for that, a technology of increasing a percentage of the data bands occupying the magnetic layer by narrowing the width of the servo band which is not a region in which information is recorded is considered. Since a read track width of the servo pattern becomes narrow, in a case where the width of the servo band becomes narrow, reading accuracy of the servo pattern tends to decrease. As a result, a Signal-to-Noise-Ratio (SNR) at the time of reading a servo pattern tends to decrease. In regards to this point, the inventors have considered that, it is desired to use a magnetic head having high sensitivity as the servo head, in order to increase an SNR at the time of reading a servo pattern. As a magnetic head for this, the inventors focused on a TMR head which has been proposed to be used as a reproducing head in the magnetic disk device in JP2004-185676A. As described above, the usage of the TMR head in the magnetic tape device is still in a stage where the future use thereof as a reproducing head for reproducing information is expected, and the usage of the TMR head as the servo head has not even proposed yet. With respect to this, the inventors have thought that, it is possible to deal with realization of higher sensitivity of the future magnetic tape, by using the TMR head as the servo head in the magnetic tape device which performs the head tracking servo. In addition, the inventors have investigated regarding a further increase in SNR in a case of reading a servo pattern by using the TMR head as a servo head. This is because, it is thought that it is possible to improve accuracy of the magnetic head following the data track by the head tracking servo, as the SNR at the time of reading a servo pattern increases.

An object of the invention is to provide a magnetic tape device in which a TMR head is mounted as a servo head and a servo pattern written on a magnetic tape can be read at a high SNR.

According to one aspect of the invention, there is provided a magnetic tape device comprising: a magnetic tape; and a servo head, in which the servo head is a magnetic head (hereinafter, also referred to as a “TMR head”) including a tunnel magnetoresistance effect type element (hereinafter, also referred to as a “TMR element”) as a servo pattern reading element, the magnetic tape includes a non-magnetic support, and a magnetic layer including ferromagnetic powder and a binding agent on the non-magnetic support, the magnetic layer includes the servo pattern, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, an intensity ratio (Int(110)/Int(114); hereinafter, also referred to as “X-ray diffraction (XRD) intensity ratio) of a peak intensity Int(110) of a diffraction peak of a (110) plane with respect to a peak intensity Int(114) of a diffraction peak of a (114) plane of a hexagonal ferrite crystal structure obtained by an X-ray diffraction analysis of the magnetic layer by using an In-Plane method is 0.5 to 4.0, and a vertical direction squareness ratio of the magnetic tape is 0.65 to 1.00.

According to another aspect of the invention, there is provided a head tracking servo method comprising: reading a servo pattern of a magnetic layer of a magnetic tape by a servo head in a magnetic tape device, in which the servo head is a magnetic head including a tunnel magnetoresistance effect type element as a servo pattern reading element, the magnetic tape includes a non-magnetic support, and a magnetic layer including ferromagnetic powder and a binding agent on the non-magnetic support, the magnetic layer includes the servo pattern, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, an intensity ratio (Int(110)/Int(114)) of a peak intensity Int(110) of a diffraction peak of a (110) plane with respect to a peak intensity Int(114) of a diffraction peak of a (114) plane of a hexagonal ferrite crystal structure obtained by an X-ray diffraction analysis of the magnetic layer by using an In-Plane method is 0.5 to 4.0, and a vertical direction squareness ratio of the magnetic tape is 0.65 to 1.00.

One aspect of the magnetic tape device and the head tracking servo method is as follows.

In one aspect, the vertical direction squareness ratio is 0.65 to 0.90.

In one aspect, a center line average surface roughness Ra measured regarding a surface of the magnetic layer (hereinafter, also referred to as a “magnetic layer surface roughness Ra”) is equal to or smaller than 2.5 nm.

In one aspect, the magnetic tape includes a non-magnetic layer including non-magnetic powder and a binding agent between the non-magnetic support and the magnetic layer.

According to one aspect of the invention, it is possible to read a servo pattern of the magnetic layer of the magnetic tape with the TMR head at a high SNR.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an example of disposition of data bands and servo bands.

FIG. 2 shows a servo pattern disposition example of a linear-tape-open (LTO) Ultrium format tape.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Magnetic Tape Device

One aspect of the invention relates to a magnetic tape device including: a magnetic tape; and a servo head, in which the servo head is a magnetic head including a tunnel magnetoresistance effect type element as a servo pattern reading element, the magnetic tape includes a non-magnetic support, and a magnetic layer including ferromagnetic powder and a binding agent on the non-magnetic support, the magnetic layer includes a servo pattern, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, an intensity ratio (Int(110)/Int(114)) of a peak intensity Int(110) of a diffraction peak of a (110) plane with respect to a peak intensity Int(114) of a diffraction peak of a (114) plane of a hexagonal ferrite crystal structure obtained by an X-ray diffraction analysis of the magnetic layer by using an In-Plane method is 0.5 to 4.0, and a vertical direction squareness ratio of the magnetic tape is 0.65 to 1.00.

In the invention and the specification, a “surface of a magnetic layer” of a magnetic tape is identical to a surface of a magnetic recording medium on a magnetic layer side. In the invention and the specification, the “ferromagnetic hexagonal ferrite powder” means an aggregate of a plurality of ferromagnetic hexagonal ferrite particles. The ferromagnetic hexagonal ferrite particles are ferromagnetic particles having a hexagonal ferrite crystal structure. Hereinafter, particles (ferromagnetic hexagonal ferrite particles) configuring the ferromagnetic hexagonal ferrite powder are also referred to as “hexagonal ferrite particles” or simply “particles”. The “aggregate” not only includes an aspect in which particles configuring the aggregate directly come into contact with each other, but also includes an aspect in which a binding agent, an additive, or the like is interposed between the particles. The points described above are also applied to various powders such as non-magnetic powder of the invention and the specification, in the same manner.

In the invention and the specification, the description regarding directions and angles (for example, vertical, orthogonal, parallel, and the like) includes a range of errors allowed in the technical field of the invention, unless otherwise noted. For example, the range of errors means a range of less than ±10° from an exact angle, and is preferably within ±5° and more preferably within ±3°.

The magnetic tape device includes a TMR head as a servo head. This can contribute to improvement of the SNR at the time of reading a servo pattern. In addition, the inventors have thought that the vertical direction squareness ratio and the XRD intensity ratio set to be in the ranges described above contribute to the reading of a servo pattern written in the magnetic layer of the magnetic tape in the magnetic tape device by using the TMR head at a high SNR. This point will be further described hereinafter.

The magnetic tape of the magnetic tape device includes ferromagnetic hexagonal ferrite powder in the magnetic layer. The inventors have surmised that particles affecting magnetic properties of the ferromagnetic hexagonal ferrite powder (aggregate of particles) (hereinafter, also referred to as “former particles”) and particles which are considered not to affect or slightly affects the magnetic properties thereof (hereinafter, also referred to as “latter particles”) are included in the ferromagnetic hexagonal ferrite powder included in the magnetic layer. It is considered that the latter particles are, for example, fine particles generated due to partial chipping of particles due to a dispersion process performed at the time of preparing a magnetic layer forming composition.

The inventors have thought that, in the particles included in the ferromagnetic hexagonal ferrite powder included in the magnetic layer, the former particles are particles causing the diffraction peak in the X-ray diffraction analysis using the In-Plane method, and since the latter particles are fine, the latter particles do not or hardly affect the diffraction peak. Accordingly, it is surmised that it is possible to control a state of the particles affecting the magnetic properties of the ferromagnetic hexagonal ferrite powder present in the magnetic layer, based on the intensity of the diffraction peak caused by the X-ray diffraction analysis of the magnetic layer using the In-Plane method. The inventors have thought that the XRD intensity ratio which will be described later specifically is an index regarding this point.

Meanwhile, the vertical direction squareness ratio is a ratio of residual magnetization with respect to saturated magnetization measured in a direction vertical to the surface of the magnetic layer and this value decreases, as a value of the residual magnetization decreases. It is surmised that, since the latter particles are fine and hardly hold magnetization, as a large amount of the latter particles is included in the magnetic layer, the vertical direction squareness ratio tends to decrease. Accordingly, the inventors have thought that the vertical direction squareness ratio may be an index for the amount of the latter particles (fine particles) present in the magnetic layer. It is thought that, as the amount of such fine particles present in the magnetic layer decreases, the magnetic properties of the ferromagnetic hexagonal ferrite powder are improved.

It is surmised that, in the magnetic tape included in the magnetic tape device, the vertical direction squareness ratio and the XRD intensity ratio respectively in the ranges described above contribute to the reading of a servo pattern written in the magnetic layer of the magnetic tape at a high SNR. The inventors have surmised that the reading at a high SNR can be realized by decreasing the amount of the latter particles (fine particles) present in the magnetic layer and controlling a state of the former particles present in the magnetic layer.

The above description is a surmise of the inventors regarding the reading of a servo pattern written in the magnetic layer of the magnetic tape at a high SNR, in the magnetic tape device.

However, the above descriptions are merely a surmise of the inventors and the invention is not limited thereto.

Hereinafter, the magnetic tape device will be described more specifically.

Magnetic Tape

XRD Intensity Ratio

The magnetic tape includes ferromagnetic hexagonal ferrite powder in the magnetic layer. The XRD intensity ratio is obtained by the X-ray diffraction analysis of the magnetic layer including the ferromagnetic hexagonal ferrite powder by using the In-Plane method. Hereinafter, the X-ray diffraction analysis performed by using the In-Plane method is also referred to as “In-Plane XRD”. The In-Plane XRD is performed by irradiating the surface of the magnetic layer with the X-ray by using a thin film X-ray diffraction device under the following conditions. A measurement direction is a longitudinal direction of the magnetic tape.

Cu ray source used (output of 45 kV, 200 mA)

Scan conditions: 0.05 degree/step, 0.1 degree/min in a range of 20 to 40 degrees

Optical system used: parallel optical system

Measurement method: 20× scan (X-ray incidence angle of 0.25°)

The values of the conditions are set values of the thin film X-ray diffraction device. As the thin film X-ray diffraction device, a well-known device can be used. As an example of the thin film X-ray diffraction device, Smart Lab manufactured by Rigaku Corporation. A sample to be subjected to the In-Plane XRD analysis is a tape sample cut out from the magnetic tape which is a measurement target, and the size and the shape thereof are not limited, as long as the diffraction peak which will be described later can be confirmed.

As a method of the X-ray diffraction analysis, thin film X-ray diffraction and powder X-ray diffraction are used. In the powder X-ray diffraction, the X-ray diffraction of the powder sample is measured, whereas, according to the thin film X-ray diffraction, the X-ray diffraction of a layer or the like formed on a substrate can be measured. The thin film X-ray diffraction is classified into the In-Plane method and an Out-Of-Plane method. The X-ray incidence angle at the time of the measurement is 5.00° to 90.00° in a case of the Out-Of-Plane method, and is generally 0.20° to 0.50°, in a case of the In-Plane method. In the In-Plane XRD of the invention and the specification, the X-ray incidence angle is 0.25° as described above. In the In-Plane method, the X-ray incidence angle is smaller than that in the Out-Of-Plane method, and thus, a depth of penetration of the X-ray is shallow. Accordingly, according to the X-ray diffraction analysis by using the In-Plane method (In-Plane XRD), it is possible to perform the X-ray diffraction analysis of a surface part of a measurement target sample. Regarding the tape sample, according to the In-Plane XRD, it is possible to perform the X-ray diffraction analysis of the magnetic layer. The XRD intensity ratio is an intensity ratio (Int(110)/Int(114)) of a peak intensity Int(110) of a diffraction peak of a (110) plane with respect to a peak intensity Int(114) of a diffraction peak of a (114) plane of a hexagonal ferrite crystal structure, in X-ray diffraction spectra obtained by the In-Plane XRD. The term Int is used as abbreviation of intensity. In the X-ray diffraction spectra obtained by In-Plane XRD (vertical axis: intensity, horizontal axis: diffraction angle 20× (degree)), the diffraction peak of the (114) plane is a peak at which the 20× is detected at 33 to 36 degrees, and the diffraction peak of the (110) plane is a peak at which the 20× is detected at 29 to 32 degrees.

Among the diffraction plane, the (114) plane having a hexagonal ferrite crystal structure is positioned close to particles (hexagonal ferrite particles) of the ferromagnetic hexagonal ferrite powder in an easy-magnetization axial direction (c axis direction). In addition the (110) plane having a hexagonal ferrite crystal structure is positioned in a direction orthogonal to the easy-magnetization axial direction.

The inventors have surmised that, in the X-ray diffraction spectra obtained by the In-Plane XRD, as the intensity ratio (Int(110)/Int(114); XRD intensity ratio) of the peak intensity Int(110) of the diffraction peak of a (110) plane with respect to the peak intensity Int(114) of the diffraction peak of the (114) plane of a hexagonal ferrite crystal structure increases, a large number of the former particles present in a state where a direction orthogonal to the easy-magnetization axial direction is closer to a parallel state with respect to the surface of the magnetic layer is present in the magnetic layer, and as the XRD intensity ratio decreases, a small amount of the former particles present in such a state is present in the magnetic layer. It is thought that a state where the XRD intensity ratio is 0.5 to 4.0 means a state where the former particles are suitably aligned in the magnetic layer. The inventors have surmised that this contributes to an increase in SNR at the time of reading a servo pattern with the TMR head.

The XRD intensity ratio is preferably equal to or smaller than 3.5 and more preferably equal to or smaller than 3.0, from a viewpoint of further increasing the SNR. From the same viewpoint, the XRD intensity ratio is preferably equal to or greater than 0.7 and more preferably equal to or greater than 1.0. The XRD intensity ratio can be, for example, controlled in accordance with process conditions of an orientation process performed in a manufacturing step of the magnetic tape. As the orientation process, the homeotropic alignment process is preferably performed. The homeotropic alignment process can be preferably performed by applying a magnetic field vertically to the surface of a coating layer of a magnetic layer forming composition in a wet state (undried state). As the orientation conditions are reinforced, the value of the XRD intensity ratio tends to increase. As the process conditions of the orientation process, magnetic field strength of the orientation process is used. The process conditions of the orientation process are not particularly limited. The process conditions of the orientation process may be set so as that the XRD intensity ratio of 0.5 to 4.0 can be realized. As an example, the magnetic field strength of the homeotropic alignment process can be 0.10 to 0.80 T or 0.10 to 0.60 T. As dispersibility of the ferromagnetic hexagonal ferrite powder in the magnetic layer forming composition increases, the value of the XRD intensity ratio tends to increase by the homeotropic alignment process.

Vertical Direction Squareness Ratio

The vertical direction squareness ratio is a squareness ratio measured regarding a magnetic tape in a vertical direction. The “vertical direction” described regarding the squareness ratio is a direction orthogonal to the surface of the magnetic layer. That is, regarding the magnetic tape, the vertical direction is a direction orthogonal to a longitudinal direction of the magnetic tape. The vertical direction squareness ratio is measured by using an oscillation sample type magnetic-flux meter. Specifically, the vertical direction squareness ratio of the invention and the specification is a value obtained by sweeping an external magnetic field in the magnetic tape at a measurement temperature of 23° C.±1° C. in the oscillation sample type magnetic-flux meter, under conditions of a maximum external magnetic field of 1194 kA/m (15 kOe) and a scan speed of 4.8 kA/m/sec (60 Oe/sec), and is a value after diamagnetic field correction. The measurement value is obtained as a value obtained by subtracting magnetization of a sample probe of the oscillation sample type magnetic-flux meter as background noise.

The vertical direction squareness ratio of the magnetic tape is equal to or greater than 0.65. The inventors have surmised that the vertical direction squareness ratio of the magnetic tape is an index for the presence amount of the latter particles (fine particles) described above. It is thought that, in the magnetic layer in which the vertical direction squareness ratio of the magnetic tape is equal to or greater than 0.65, the presence amount of such fine particles is small. The inventors have surmised that this contributes to an increase in SNR at the time of reading a servo pattern of the magnetic layer with the TMR head. From a viewpoint of further increasing the SNR, the vertical direction squareness ratio is preferably equal to or greater than 0.70, more preferably equal to or greater than 0.73, and even more preferably equal to or greater than 0.75. In addition, in principle, a maximum value of the squareness ratio is 1.00. Accordingly, the vertical direction squareness ratio of the magnetic tape is equal to or smaller than 1.00. The vertical direction squareness ratio may be, for example, equal to or smaller than 0.95, equal to or smaller than 0.90, equal to or smaller than 0.87, or equal to or smaller than 0.85. However, it is thought that, a great value of the vertical direction squareness ratio is preferable, from a viewpoint of decreasing the amount of the latter fine particles in the magnetic layer and increasing the SNR. Therefore, the vertical direction squareness ratio may be greater than the value exemplified above.

The inventors have considered that, in order to set the vertical direction squareness ratio to be equal to or greater than 0.65, it is preferable to prevent occurrence of fine particles due to partial chipping of the particles in a preparation step of the magnetic layer forming composition. A specific method for preventing the occurrence of chipping will be described later.

Next, the magnetic layer and the like included in the magnetic tape will be described more specifically.

Magnetic Layer

Ferromagnetic Powder

The magnetic layer of the magnetic tape includes ferromagnetic hexagonal ferrite powder as ferromagnetic powder. Regarding the ferromagnetic hexagonal ferrite powder, a magnetoplumbite type (also referred to as an “M type”), a W type, a Y type, and a Z type are known as the crystal structure of the hexagonal ferrite. The ferromagnetic hexagonal ferrite powder included in the magnetic layer may have any crystal structure. In addition, an iron atom and a divalent metal atom are included in the crystal structure of the hexagonal ferrite, as constituent atoms. The divalent metal atom is a metal atom which may become divalent cations as ions, and examples thereof include a barium atom, a strontium atom, an alkaline earth metal atom such as calcium atom, and a lead atom. For example, the hexagonal ferrite including a barium atom as the divalent metal atom is a barium ferrite, and the hexagonal ferrite including a strontium atom is a strontium ferrite. In addition, the hexagonal ferrite may be a mixed crystal of two or more hexagonal ferrites. As an example of the mixed crystal, a mixed crystal of the barium ferrite and the strontium ferrite can be used.

As an index for a particle size of the ferromagnetic hexagonal ferrite powder, an activation volume can be used. The “activation volume” is a unit of magnetization reversal. Regarding the activation volume described in the invention and the specification, magnetic field sweep rates of a coercivity Hc measurement part at time points of 3 minutes and 30 minutes are measured by using an oscillation sample type magnetic-flux meter in an environment of an atmosphere temperature of 23° C.±1° C., and the activation volume is a value acquired from the following relational expression of Hc and an activation volume V. Hc=2Ku/Ms{1−[(kT/KuV)ln(At/0.693)]^(1/2)}

[In the expression, Ku: anisotropy constant, Ms: saturation magnetization, k: Boltzmann's constant, T: absolute temperature, V: activation volume, A: spin precession frequency, and t: magnetic field reversal time]

As a method for achieving high-density recording, a method of decreasing a particle size of ferromagnetic powder included in a magnetic layer and increasing a filling percentage of the ferromagnetic powder of the magnetic layer is used. From this viewpoint, the activation volume of the ferromagnetic hexagonal ferrite powder is preferably equal to or smaller than 2,500 nm³, more preferably equal to or smaller than 2,300 nm³, and even more preferably equal to or smaller than 2,000 nm³. Meanwhile, from a viewpoint of stability of magnetization, the activation volume is, for example, preferably equal to or greater than 800 nm³, more preferably equal to or greater than 1,000 nm³, and even more preferably equal to or greater than 1,200 nm³. An activation volume of the ferromagnetic hexagonal ferrite powder used for preparing the magnetic layer forming composition (hereinafter, also referred to as “raw material powder”) and an activation volume of the ferromagnetic hexagonal ferrite powder in the magnetic layer formed by using the prepared magnetic layer forming composition may be the same as each other or different from each other.

The shape of the particle configuring the ferromagnetic hexagonal ferrite powder is specified by imaging the ferromagnetic hexagonal ferrite powder at a magnification ratio of 100,000 with a transmission electron microscope, and tracing an outline of a particle (primary particle) with a digitizer on a particle image obtained by printing the image on printing paper so that the total magnification of 500,000. The primary particle is an independent particle which is not aggregated. The imaging with a transmission electron microscope is performed by a direct method with a transmission electron microscope at an acceleration voltage of 300 kV. The transmission electron microscope observation and measurement can be, for example, performed with a transmission electron microscope H-9000 manufactured by Hitachi, Ltd. and image analysis software KS-400 manufactured by Carl Zeiss. Regarding the shape of the particle configuring the ferromagnetic hexagonal ferrite powder, a “planar shape” is a shape having two plate surfaces facing each other. Meanwhile, among the shapes of the particles not having such a plate surface, a shape having distinguished long axis and short axis is an “elliptical shape”. The long axis is determined as an axis (linear line) having the longest length of the particle. In contrast, the short axis is determined as an axis having the longest length of the particle in a linear line orthogonal to the long axis. A shape not having distinguished long axis and short axis, that is, a shape in which the length of the long axis is the same as the length of the short axis is a “spherical shape”. From the shapes, a shape in which the long axis and the short axis are hardly specified, is called an undefined shape. The imaging with a transmission electron microscope for specifying the shapes of the particles is performed without performing the orientation process with respect to the imaging target powder. The shape of the raw material powder used for the preparation of the magnetic layer forming composition and the ferromagnetic hexagonal ferrite powder included in the magnetic layer may be any one of the planar shape, the elliptical shape, the spherical shape, and the undefined shape.

An average particle size of various powders disclosed in the invention and the specification is an arithmetical mean of the values obtained regarding arbitrarily extracted 500 particles by using the particle image which is captured as described above. The average particle size shown in the examples which will be described later is a value obtained by using transmission electron microscope H-9000 manufactured by Hitachi, Ltd. as the transmission electron microscope and image analysis software KS-400 manufactured by Carl Zeiss as the image analysis software.

For details of the ferromagnetic hexagonal ferrite powder, descriptions disclosed in paragraphs 0134 to 0136 of JP2011-216149A can be referred to, for example.

The content (filling percentage) of the ferromagnetic hexagonal ferrite powder in the magnetic layer is preferably 50 to 90 mass % and more preferably 60 to 90 mass %. The components other than the ferromagnetic hexagonal ferrite powder of the magnetic layer are at least a binding agent, and one or more kinds of additives may be arbitrarily included. A high filling percentage of the ferromagnetic hexagonal ferrite powder in the magnetic layer is preferable from a viewpoint of improvement recording density.

Binding Agent

The magnetic tape is a coating type magnetic tape, and the magnetic layer includes a binding agent together with the ferromagnetic powder. As the binding agent, one or more kinds of resin is used. The resin may be a homopolymer or a copolymer. As the binding agent, various resins normally used as a binding agent of the coating type magnetic recording medium can be used. For example, as the binding agent, a resin selected from a polyurethane resin, a polyester resin, a polyamide resin, a vinyl chloride resin, an acrylic resin obtained by copolymerizing styrene, acrylonitrile, or methyl methacrylate, a cellulose resin such as nitrocellulose, an epoxy resin, a phenoxy resin, and a polyvinylalkylal resin such as polyvinyl acetal or polyvinyl butyral can be used alone or a plurality of resins can be mixed with each other to be used. Among these, a polyurethane resin, an acrylic resin, a cellulose resin, and a vinyl chloride resin are preferable. These resins can be used as the binding agent even in the non-magnetic layer and/or a back coating layer which will be described later. For the binding agent described above, description disclosed in paragraphs 0028 to 0031 of JP2010-24113A can be referred to. An average molecular weight of the resin used as the binding agent can be, for example, 10,000 to 200,000 as a weight-average molecular weight. The weight-average molecular weight of the invention and the specification is a value obtained by performing polystyrene conversion of a value measured by gel permeation chromatography (GPC). As the measurement conditions, the following conditions can be used. The weight-average molecular weight shown in examples which will be described later is a value obtained by performing polystyrene conversion of a value measured under the following measurement conditions.

GPC device: HLC-8120 (manufactured by Tosoh Corporation)

Column: TSK gel Multipore HXL-M (manufactured by Tosoh Corporation, 7.8 mmID (inner diameter)×30.0 cm)

Eluent: Tetrahydrofuran (THF)

In addition, a curing agent can also be used together with the binding agent. As the curing agent, in one aspect, a thermosetting compound which is a compound in which a curing reaction (crosslinking reaction) proceeds due to heating can be used, and in another aspect, a photocurable compound in which a curing reaction (crosslinking reaction) proceeds due to light irradiation can be used. At least a part of the curing agent is included in the magnetic layer in a state of being reacted (crosslinked) with other components such as the binding agent, by proceeding the curing reaction in the magnetic layer forming step. The preferred curing agent is a thermosetting compound, polyisocyanate is suitable. For details of the polyisocyanate, descriptions disclosed in paragraphs 0124 and 0125 of JP2011-216149A can be referred to, for example. The amount of the curing agent can be, for example, 0 to 80.0 parts by mass with respect to 100.0 parts by mass of the binding agent in the magnetic layer forming composition, and is preferably 50.0 to 80.0 parts by mass, from a viewpoint of improvement of strength of each layer such as the magnetic layer.

Other Components

The magnetic layer may include one or more kinds of additives, if necessary, together with the various components described above. As the additives, a commercially available product can be suitably selected and used according to the desired properties. Alternatively, a compound synthesized by a well-known method can be used as the additives. As the additives, the curing agent described above is used as an example. In addition, examples of the additive which can be included in the magnetic layer include a non-magnetic filler, a lubricant, a dispersing agent, a dispersing assistant, an antibacterial agent, an antistatic agent, an antioxidant, and carbon black. The non-magnetic filler is identical to the non-magnetic powder. As the non-magnetic filler, a non-magnetic filler (hereinafter, referred to as a “projection formation agent”) which can function as a projection formation agent which forms projections suitably protruded from the surface of the magnetic layer, and a non-magnetic filler (hereinafter, referred to as an “abrasive”) which can function as an abrasive can be used.

Non-Magnetic Filler

As the projection formation agent which is one aspect of the non-magnetic filler, various non-magnetic powders normally used as a projection formation agent can be used. These may be inorganic substances or organic substances. In one aspect, from a viewpoint of homogenization of friction properties, particle size distribution of the projection formation agent is not polydispersion having a plurality of peaks in the distribution and is preferably monodisperse showing a single peak. From a viewpoint of availability of monodisperse particles, the projection formation agent is preferably powder of inorganic substances (inorganic powder). Examples of the inorganic powder include powder of inorganic oxide such as metal oxide, metal carbonate, metal sulfate, metal nitride, metal carbide, and metal sulfide, and powder of inorganic oxide is preferable. The projection formation agent is more preferably colloidal particles and even more preferably inorganic oxide colloidal particles. In addition, from a viewpoint of availability of monodisperse particles, the inorganic oxide configuring the inorganic oxide colloidal particles are preferably silicon dioxide (silica). The inorganic oxide colloidal particles are more preferably colloidal silica (silica colloidal particles). In the invention and the specification, the “colloidal particles” are particles which are not precipitated and dispersed to generate a colloidal dispersion, in a case where 1 g of the particles is added to 100 mL of at least one organic solvent of at least methyl ethyl ketone, cyclohexanone, toluene, or ethyl acetate, or a mixed solvent including two or more kinds of the solvent described above at an arbitrary mixing ratio. The average particle size of the colloidal particles is a value obtained by a method disclosed in a paragraph 0015 of JP2011-048878A as a measurement method of an average particle diameter. In addition, in another aspect, the projection formation agent is preferably carbon black.

An average particle size of the projection formation agent is, for example, 30 to 300 nm and is preferably 40 to 200 nm.

The abrasive which is another aspect of the non-magnetic filler is preferably non-magnetic powder having Mohs hardness exceeding 8 and more preferably non-magnetic powder having Mohs hardness equal to or greater than 9. A maximum value of Mohs hardness is 10 of diamond. Specifically, powders of alumina (Al₂O₃), silicon carbide, boron carbide (B₄C), SiO₂, TiC, chromium oxide (Cr₂O₃), cerium oxide, zirconium oxide (ZrO₂), iron oxide, diamond, and the like can be used, and among these, alumina powder such as α-alumina and silicon carbide powder are preferable. In addition, regarding the particle size of the abrasive, a specific surface area which is an index for the particle size is, for example, equal to or greater than 14 m²/g, and is preferably 16 m²/g and more preferably 18 m²/g. Further, the specific surface area of the abrasive can be, for example, equal to or smaller than 40 m²/g. The specific surface area is a value obtained by a nitrogen adsorption method (also referred to as a Brunauer-Emmett-Teller (BET) 1 point method), and is a value measured regarding primary particles. Hereinafter, the specific surface area obtained by such a method is also referred to as a BET specific surface area.

In addition, from a viewpoint that the projection formation agent and the abrasive can exhibit the functions thereof in more excellent manner, the content of the projection formation agent of the magnetic layer is preferably 1.0 to 4.0 parts by mass and more preferably 1.5 to 3.5 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder. Meanwhile, the content of the magnetic layer is preferably 1.0 to 20.0 parts by mass, more preferably 3.0 to 15.0 parts by mass, and even more preferably 4.0 to 10.0 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder.

As an example of the additive which can be used in the magnetic layer including the abrasive, a dispersing agent disclosed in paragraphs 0012 to 0022 of JP2013-131285A can be used as a dispersing agent for improving dispersibility of the abrasive of the magnetic layer forming composition. It is preferable to improve dispersibility of the magnetic layer forming composition of the non-magnetic filler such as an abrasive, in order to decrease the magnetic layer surface roughness Ra which will be described later in detail.

In addition, as the dispersing agent, a well-known dispersing agent such as a carboxy group-containing compound or a nitrogen-containing compound can be used. For example, the nitrogen-containing compound may be any of a primary amine represented by NH₂R, a secondary amine represented by NHR₂, and a tertiary amine represented by NR₃. In the above description, R represents an arbitrary structure configuring the nitrogen-containing compound, and a plurality of Rs may be the same as each other or different from each other. The nitrogen-containing compound may be a compound (polymer) having a plurality of repeating structure in a molecule. The inventors have thought that a nitrogen-containing part of the nitrogen-containing compound which functions as an adsorption part to the surface of the particle of the ferromagnetic hexagonal ferrite powder is a reason why the nitrogen-containing compound can function as the dispersing agent. As the carboxy group-containing compound, fatty acid such as oleic acid can be used, for example. The inventors have thought that a carboxy group which functions as an adsorption part to the surface of the particle of the ferromagnetic powder is a reason why the carboxy group-containing compound can function as the dispersing agent. It is also preferable to use the carboxy group-containing compound and the nitrogen-containing compound in combination.

Magnetic Layer Surface Roughness Ra

In the magnetic tape, in one preferred aspect, the center line average surface roughness Ra measured regarding the surface of the magnetic layer (magnetic layer surface roughness Ra) can be equal to or smaller than 2.5 nm. From a viewpoint of increasing the SNR, the magnetic layer surface roughness Ra is preferably equal to or smaller than 2.5 nm. From a viewpoint of further increasing the SNR, the magnetic layer surface roughness Ra is preferably equal to or smaller than 2.4 nm, more preferably equal to or smaller than 2.3 nm, even more preferably equal to or smaller than 2.2 nm, still preferably equal to or smaller than 2.1 nm, and still more preferably equal to or smaller than 2.0 nm. In addition, the magnetic layer surface roughness Ra can be, for example, equal to or greater than 1.0 nm or equal to or greater than 1.2 nm. However, from a viewpoint of increasing the SNR at the time of reading a servo pattern, a low magnetic layer surface roughness Ra is preferable, and thus, the magnetic layer surface roughness Ra may be lower than the lower limit exemplified above.

The center line average surface roughness Ra measured regarding the surface of the magnetic layer of the magnetic tape in the invention and the specification is a value measured with an atomic force microscope (AFM) in a region having an area of 40 μm×40 μm of the surface of the magnetic layer. As an example of the measurement conditions, the following measurement conditions can be used. The magnetic layer surface roughness Ra shown in examples which will be described later is a value obtained by the measurement under the following measurement conditions.

The measurement is performed regarding the region of 40 μm×40 μm of the area of the surface of the magnetic layer of the magnetic tape with an AFM (Nanoscope 4 manufactured by Veeco Instruments, Inc.) in a tapping mode. RTESP-300 manufactured by BRUKER is used as a probe, a scan speed (probe movement speed) is set as 40 μm/sec, and a resolution is set as 512 pixel×512 pixel.

The magnetic layer surface roughness Ra can be controlled by a well-known method. For example, the magnetic layer surface roughness Ra can be changed in accordance with the size of various powders included in the magnetic layer or manufacturing conditions of the magnetic tape. Thus, by adjusting one or more of these, it is possible to control the magnetic layer surface roughness Ra.

Non-Magnetic Layer

Next, the non-magnetic layer will be described. The magnetic tape may include a magnetic layer directly on a non-magnetic support, or may include a non-magnetic layer including non-magnetic powder and a binding agent between the non-magnetic support and the magnetic layer. The non-magnetic powder used in the non-magnetic layer may be powder of inorganic substances or powder of organic substances. In addition, carbon black and the like can be used. Examples of the inorganic substances include metal, metal oxide, metal carbonate, metal sulfate, metal nitride, metal carbide, and metal sulfide. These non-magnetic powder can be purchased as a commercially available product or can be manufactured by a well-known method. For details thereof, descriptions disclosed in paragraphs 0146 to 0150 of JP2011-216149A can be referred to. For carbon black which can be used in the non-magnetic layer, descriptions disclosed in paragraphs 0040 and 0041 of JP2010-24113A can be referred to. The content (filling percentage) of the non-magnetic powder of the non-magnetic layer is preferably 50 to 90 mass % and more preferably 60 to 90 mass %.

In regards to other details of a binding agent or additives of the non-magnetic layer, the well-known technology regarding the non-magnetic layer can be applied. In addition, in regards to the type and the content of the binding agent, and the type and the content of the additive, for example, the well-known technology regarding the magnetic layer can be applied.

The non-magnetic layer of the magnetic tape also includes a substantially non-magnetic layer including a small amount of ferromagnetic powder as impurities or intentionally, together with the non-magnetic powder. Here, the substantially non-magnetic layer is a layer having a residual magnetic flux density equal to or smaller than 10 mT, a layer having coercivity equal to or smaller than 7.96 kA/m (100 Oe), or a layer having a residual magnetic flux density equal to or smaller than 10 mT and coercivity equal to or smaller than 7.96 kA/m (100 Oe). It is preferable that the non-magnetic layer does not have a residual magnetic flux density and coercivity.

Non-Magnetic Support

Next, the non-magnetic support will be described. As the non-magnetic support (hereinafter, also simply referred to as a “support”), well-known components such as polyethylene terephthalate, polyethylene naphthalate, polyamide, polyamide imide, aromatic polyamide subjected to biaxial stretching are used. Among these, polyethylene terephthalate, polyethylene naphthalate, and polyamide are preferable. Corona discharge, plasma treatment, easy-bonding treatment, or heating treatment may be performed with respect to these supports in advance.

Back Coating Layer

The magnetic tape can also include a back coating layer including non-magnetic powder and a binding agent on a surface side of the non-magnetic support opposite to the surface provided with the magnetic layer. The back coating layer preferably includes any one or both of carbon black and inorganic powder. In regards to the binding agent included in the back coating layer and various additives which can be arbitrarily included in the back coating layer, a well-known technology regarding the treatment of the magnetic layer and/or the non-magnetic layer can be applied.

Various Thickness

A thickness of the non-magnetic support is preferably 3.00 to 6.00 μm.

A thickness of the magnetic layer is preferably equal to or smaller than 0.15 μm and more preferably equal to or smaller than 0.10 μm, from a viewpoint of realization of high-density recording required in recent years. The thickness of the magnetic layer is even more preferably 0.01 to 0.10 μm. The magnetic layer may be at least single layer, the magnetic layer may be separated into two or more layers having different magnetic properties, and a configuration of a well-known multilayered magnetic layer can be applied. A thickness of the magnetic layer in a case where the magnetic layer is separated into two or more layers is a total thickness of the layers.

A thickness of the non-magnetic layer is, for example, 0.10 to 1.50 μm and is preferably 0.10 to 1.00 μm.

Meanwhile, the magnetic tape is normally used to be accommodated and circulated in a magnetic tape cartridge. In order to increase recording capacity for 1 reel of the magnetic tape cartridge, it is desired to increase a total length of the magnetic tape accommodated in 1 reel of the magnetic tape cartridge. In order to increase the recording capacity, it is necessary that the magnetic tape is thinned (hereinafter, referred to as “thinning”). As one method of thinning the magnetic tape, a method of decreasing a total thickness of a magnetic layer and a non-magnetic layer of a magnetic tape including the non-magnetic layer and the magnetic layer on a non-magnetic support in this order is used. In a case where the magnetic tape includes a non-magnetic layer, the total thickness of the magnetic layer and the non-magnetic layer is preferably equal to or smaller than 1.80 μm, more preferably equal to or smaller than 1.50 μm, and even more preferably equal to or smaller than 1.10 μm, from a viewpoint of thinning the magnetic tape. In addition, the total thickness of the magnetic layer and the non-magnetic layer can be, for example, equal to or greater than 0.10 μm.

A thickness of the back coating layer is preferably equal to or smaller than 0.90 μm and even more preferably 0.10 to 0.70 μm.

The thicknesses of various layers of the magnetic tape and the non-magnetic support can be acquired by a well-known film thickness measurement method. As an example, a cross section of the magnetic tape in a thickness direction is, for example, exposed by a well-known method of ion beams or microtome, and the exposed cross section is observed with a scanning electron microscope. In the cross section observation, various thicknesses can be acquired as a thickness acquired at one position of the cross section in the thickness direction, or an arithmetical mean of thicknesses acquired at a plurality of positions of two or more positions, for example, two positions which are arbitrarily extracted. In addition, the thickness of each layer may be acquired as a designed thickness calculated according to the manufacturing conditions.

Manufacturing Method

Preparation of Each Layer Forming Composition

Each composition for forming the magnetic layer, the non-magnetic layer, or the back coating layer normally includes a solvent, together with various components described above. As the solvent, various organic solvents generally used for manufacturing a coating type magnetic recording medium can be used. Among those, from a viewpoint of solubility of the binding agent normally used in the coating type magnetic recording medium, each layer forming composition preferably includes one or more ketone solvents such as acetone, methyl ethyl ketone, methyl isobutyl ketone, diisobutyl ketone, cyclohexanone, isophorone, and tetrahydrofuran. The amount of the solvent of each layer forming composition is not particularly limited, and can be set to be the same as that of each layer forming composition of a typical coating type magnetic recording medium. In addition, steps of preparing each layer forming composition generally include at least a kneading step, a dispersing step, and a mixing step provided before and after these steps, if necessary. Each step may be divided into two or more stages. All of raw materials used in the invention may be added at an initial stage or in a middle stage of each step. In addition, each raw material may be separately added in two or more steps. For example, a binding agent may be separately added in a kneading step, a dispersing step, and a mixing step for adjusting viscosity after the dispersion. In a manufacturing step of the magnetic tape, a well-known manufacturing technology of the related art can be used in a part of the step or in the entire step. In the kneading step, an open kneader, a continuous kneader, a pressure kneader, or a kneader having a strong kneading force such as an extruder is preferably used. The details of the kneading processes of these kneaders are disclosed in JP1989-106338A (JP-H01-106338A) and JP1989-79274A (JP-H01-79274A). In addition, in order to disperse each layer forming composition, glass beads and/or other beads can be used. As such dispersion beads, zirconia beads, titania beads, and steel beads which are dispersion beads having high specific gravity are preferable. These dispersion beads are preferably used by optimizing a bead diameter and a filling percentage. As a dispersing machine, a well-known dispersing machine can be used. Each layer forming composition may be filtered by a well-known method before performing the coating step. The filtering can be performed by using a filter, for example. As the filter used in the filtering, a filter having a hole diameter of 0.01 to 3 μm can be used, for example.

Regarding the dispersion process of the magnetic layer forming composition, it is preferable to prevent the occurrence of chipping as described above. In order to realize the prevention, it is preferable to perform the dispersion process of the ferromagnetic hexagonal ferrite powder by a dispersion process having two stages, in which a coarse aggregate of the ferromagnetic hexagonal ferrite powder is crushed by the dispersion process in a first stage, and the dispersion process in a second stage, in which a collision energy applied to particles of the ferromagnetic hexagonal ferrite powder due to collision with the dispersion beads is smaller than that in the first dispersion process, is performed, in the step of preparing the magnetic layer forming composition. According to such a dispersion process, it is possible to improve dispersibility of the ferromagnetic hexagonal ferrite powder and prevent the occurrence of chipping.

As a preferred aspect of the dispersion process having two stages, a dispersion process including a first stage of obtaining a dispersion liquid by performing the dispersion process of the ferromagnetic hexagonal ferrite powder, the binding agent, and the solvent under the presence of first dispersion beads, and a second stage of performing the dispersion process of the dispersion liquid obtained in the first stage under the presence of second dispersion beads having smaller bead diameter and density than those of the first dispersion beads can be used. Hereinafter, the dispersion process of the preferred aspect described above will be further described.

In order to increase the dispersibility of the ferromagnetic hexagonal ferrite powder, the first stage and the second stage are preferably performed as the dispersion process before mixing the ferromagnetic hexagonal ferrite powder and other powder components. For example, in a case of forming the magnetic layer including the non-magnetic filler, the first stage and the second stage are preferably performed as a dispersion process of a solution (magnetic solution) including ferromagnetic hexagonal ferrite powder, a binding agent, a solvent, and arbitrarily added additives, before mixing the non-magnetic filler.

A bead diameter of the second dispersion bead is preferably equal to or smaller than 1/100 and more preferably equal to or smaller than 1/500 of a bead diameter of the first dispersion bead. The bead diameter of the second dispersion bead can be, for example, equal to or greater than 1/10,000 of the bead diameter of the first dispersion bead. However, there is no limitation to this range. The bead diameter of the second dispersion bead is, for example, preferably 80 to 1,000 nm. Meanwhile, the bead diameter of the first dispersion bead can be, for example, 0.2 to 1.0 mm.

The bead diameter of the invention and the specification is a value measured by the same method as the measurement method of the average particle size of the powder described above.

The second stage is preferably performed under the conditions in which the amount of the second dispersion beads is equal to or greater than 10 times of the amount of the ferromagnetic hexagonal ferrite powder, and is more preferably performed under the conditions in which the amount of the second dispersion beads is 10 times to 30 times of the amount of the ferromagnetic hexagonal ferrite powder, based on mass.

Meanwhile, the amount of the dispersion beads in the first stage is preferably in the range described above.

The second dispersion beads are beads having lower density than that of the first dispersion beads. The “density” is obtained by dividing the mass (unit: g) of the dispersion beads by volume (unit: cm³). The measurement is performed by the Archimedes method. The density of the second dispersion beads is preferably equal to or lower than 3.7 g/cm³ and more preferably equal to or lower than 3.5 g/cm³. The density of the second dispersion beads may be, for example, equal to or higher than 2.0 g/cm³ or may be lower than 2.0 g/cm³. As the preferred second dispersion beads from a viewpoint of density, diamond beads, silicon carbide beads, or silicon nitride beads can be used, and as preferred second dispersion beads from a viewpoint of density and hardness, diamond beads can be used.

Meanwhile, as the first dispersion beads, dispersion beads having density exceeding 3.7 g/cm³ are preferable, dispersion beads having density equal to or higher than 3.8 g/cm³ are more preferable, and dispersion beads having density equal to or higher than 4.0 g/cm³ are even more preferable. The density of the first dispersion beads may be, for example, equal to or smaller than 7.0 g/cm³ or may exceed 7.0 g/cm³. As the first dispersion beads, zirconia beads or alumina beads are preferably used, and zirconia beads are more preferably used.

The dispersion time is not particularly limited and may be set in accordance with the kind of a dispersing machine used.

Coating Step

The magnetic layer can be formed by directly applying the magnetic layer forming composition onto the surface of the non-magnetic support or performing multilayer coating of the magnetic layer forming composition with the non-magnetic layer forming composition in order or at the same time. The back coating layer can be formed by applying the back coating layer forming composition to the surface side of the non-magnetic support opposite to a surface side provided with the magnetic layer (or to be provided with the magnetic layer). For details of the coating for forming each layer, a description disclosed in a paragraph 0066 of JP2010-231843A can be referred to.

Other Steps

For details of various other steps for manufacturing the magnetic tape, descriptions disclosed in paragraphs 0067 to 0070 of JP2010-231843A can be referred to. It is preferable that the coating layer of the magnetic layer forming composition is subjected to an orientation process, while the coating layer is wet (not dried). For the orientation process, various well-known technologies such as a description disclosed in a paragraph 0067 of JP2010-231843A can be used without any limitation. As described above, it is preferable to perform the homeotropic alignment process as the orientation process, from a viewpoint of controlling the XRD intensity ratio. Regarding the orientation process, the above description can also be referred to.

As described above, it is possible to obtain a magnetic tape included in the magnetic tape device according to one aspect of the invention. However, the manufacturing method described above is merely an example, the XRD intensity ratio and the vertical direction squareness ratio can be controlled to be in respective ranges described above by an arbitrary method capable of adjusting the XRD intensity ratio and the vertical direction squareness ratio, and such an aspect is also included in the invention.

Formation of Servo Pattern

A servo pattern is formed in the magnetic layer by magnetizing a specific position of the magnetic layer with a servo pattern recording head (also referred to as a “servo write head”). A well-known technology regarding a servo pattern of the magnetic layer of the magnetic tape which is well known can be applied for the shapes of the servo pattern with which the head tracking servo can be performed and the disposition thereof in the magnetic layer. For example, as a head tracking servo system, a timing-based servo system and an amplitude-based servo system are known. The servo pattern of the magnetic layer of the magnetic tape may be a servo pattern capable of allowing head tracking servo of any system. In addition, a servo pattern capable of allowing head tracking servo in the timing-based servo system and a servo pattern capable of allowing head tracking servo in the amplitude-based servo system may be formed in the magnetic layer.

The magnetic tape described above is generally accommodated in a magnetic tape cartridge and the magnetic tape cartridge is mounted in the magnetic tape device. In the magnetic tape cartridge, the magnetic tape is generally accommodated in a cartridge main body in a state of being wound around a reel. The reel is rotatably provided in the cartridge main body. As the magnetic tape cartridge, a single reel type magnetic tape cartridge including one reel in a cartridge main body and a twin reel type magnetic tape cartridge including two reels in a cartridge main body are widely used. In a case where the single reel type magnetic tape cartridge is mounted in the magnetic tape device (drive) in order to record and/or reproduce information (magnetic signals) to the magnetic tape, the magnetic tape is drawn from the magnetic tape cartridge and wound around the reel on the drive side. A servo head is disposed on a magnetic tape transportation path from the magnetic tape cartridge to a winding reel. Sending and winding of the magnetic tape are performed between a reel (supply reel) on the magnetic tape cartridge side and a reel (winding reel) on the drive side. In the meantime, the servo head comes into contact with and slides on the surface of the magnetic layer of the magnetic tape, and accordingly, the reading of the servo pattern is performed by the servo head. With respect to this, in the twin reel type magnetic tape cartridge, both reels of the supply reel and the winding reel are provided in the magnetic tape cartridge. The magnetic tape according to one aspect of the invention may be accommodated in any of single reel type magnetic tape cartridge and twin reel type magnetic tape cartridge. The configuration of the magnetic tape cartridge is well known.

Servo Head

The magnetic tape device includes the TMR head as the servo head. A magnetoresistance effect which is an operating principle of the MR head such as the TMR head is a phenomenon in which electric resistance changes depending on a change in magnetic field. The MR head detects a change in leakage magnetic field generated from a magnetic recording medium such as a magnetic tape as a change in resistance value (electric resistance) and reads a servo pattern by converting the change in resistance value into a change in voltage. The tunnel magnetoresistance effect type element (TMR element) included in the TMR head can play a role of detecting a change in leakage magnetic field from the magnetic tape as a change in resistance value (electric resistance) by using a tunnel magnetoresistance effect, as a servo pattern reading element for reading a servo pattern formed in the magnetic layer of the magnetic tape. By converting the detected change in resistance value into a change in voltage, the servo pattern can be read (servo signal can be reproduced).

As the TMR head included in the magnetic tape device, a TMR head having a well-known configuration including a tunnel magnetoresistance effect type element (TMR element) can be used. For example, for details of the structure of the TMR head, materials of each unit configuring the TMR head, and the like, well-known technologies regarding the TMR head can be used.

The TMR head is a so-called thin film head. The TMR element included in the TMR head at least includes two electrode layers, a tunnel barrier layer, a free layer, and a fixed layer. The TMR head includes a TMR element in a state where cross sections of these layers face a side of a surface sliding on the magnetic tape. The tunnel barrier layer is positioned between the two electrode layers and the tunnel barrier layer is an insulating layer. Meanwhile, the free layer and the fixed layer are magnetic layers. The free layer is also referred to as a magnetization free layer and is a layer in which a magnetization direction changes depending on the external magnetic field. On the other hand, the fixed layer is a layer in which a magnetization direction does not change depending on the external magnetic field. The tunnel barrier layer (insulating layer) is positioned between the two electrodes, normally, and thus, even in a case where a voltage is applied, in general, a current does not flow or does not substantially flow. However, a current (tunnel current) flows by the tunnel effect depending on a magnetization direction of the free layer affected by a leakage magnetic field from the magnetic tape. The amount of a tunnel current flow changes depending on a relative angle of a magnetization direction of the fixed layer and a magnetization direction of the free layer, and as the relative angle decreases, the amount of the tunnel current flow increases. A change in amount of the tunnel current flow is detected as a change in resistance value by the tunnel magnetoresistance effect. By converting the change in resistance value into a change in voltage, the servo pattern can be read. For an example of the configuration of the TMR head, a description disclosed in FIG. 1 of JP2004-185676A can be referred to, for example. However, there is no limitation to the aspect shown in the drawing. FIG. 1 of JP2004-185676A shows two electrode layers and two shield layers. Here, a TMR head having a configuration in which the shield layer serves as an electrode layer is also well known and the TMR head having such a configuration can also be used. In the TMR head, a current (tunnel current) flows between the two electrodes and thereby changing electric resistance, by the tunnel magnetoresistance effect.

Examples of a structure of the MR head include a current-in-plane (CIP) structure and a current-perpendicular-to-plane (CPP) structure. For example, a spin valve type GMR head which is widely used in recent years among the GMR heads has a CIP structure. In the MR head having a CIP structure, a current flows in a direction in a film plane of an MR element, that is, a direction perpendicular to a direction in which the magnetic tape is transported, in a case of reproducing information recorded on the magnetic tape. With respect to this, in the MR head having a CPP structure, a current flows in a direction perpendicular to a film surface of an MR element, that is, a direction in which the magnetic tape is transported, in a case of reproducing information recorded on the magnetic tape. The TMR head is the MR head having a CPP structure.

In one preferred aspect of the magnetic tape device including the TMR head and the magnetic tape described above, it is possible to perform the head tracking servo by using the TMR head as the servo head in a case of recording information on the magnetic layer having a servo pattern at linear recording density equal to or greater than 250 kfci and/or reproducing information recorded. The unit, kfci, is a unit of linear recording density (not able to convert to the SI unit system). The linear recording density can be, for example, equal to or greater than 250 kfci and can also be equal to or greater than 300 kfci. The linear recording density can be, for example, equal to or smaller than 800 kfci and can also exceed 800 kfci. In the magnetic tape for high-density recording, a width of the servo band tends to decrease, in order to provide a large amount of data bands in the magnetic layer, and thus, the SNR at the time of reading a servo pattern easily decrease. However, a decrease in SNR can be prevented by setting the XRD intensity ratio and the vertical direction squareness ratio of the magnetic tape in the magnetic tape device to be in the ranges described above.

The servo head is a magnetic head including at least the TMR element as a servo pattern reading element. The servo head may include or may not include a reproducing element for reproducing information recorded on the magnetic tape. That is, the servo head and the reproducing head may be one magnetic head or separated magnetic heads. The same applies to a recording element for performing the recording of information in the magnetic tape.

Head Tracking Servo Method

One aspect of the invention relates to a head tracking servo method including: reading a servo pattern of a magnetic layer of a magnetic tape by a servo head in a magnetic tape device, in which the servo head is a magnetic head including a tunnel magnetoresistance effect type element as a servo pattern reading element, the magnetic tape includes a non-magnetic support, and a magnetic layer including ferromagnetic powder and a binding agent on the non-magnetic support, the magnetic layer includes the servo pattern, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, an intensity ratio (Int(110)/Int(114)) of a peak intensity Int(110) of a diffraction peak of a (110) plane with respect to a peak intensity Int(114) of a diffraction peak of a (114) plane of a hexagonal ferrite crystal structure obtained by an X-ray diffraction analysis of the magnetic layer by using an In-Plane method, that is, an XRD intensity ratio is 0.5 to 4.0, and a vertical direction squareness ratio of the magnetic tape is 0.65 to 1.00. The reading of the servo pattern is performed by bringing the magnetic tape into contact with the servo head allowing sliding while transporting (causing running of) the magnetic tape. The details of the magnetic tape and the servo head used in the head tracking servo method are as the descriptions regarding the magnetic tape device according to one aspect of the invention.

Hereinafter, as one specific aspect of the head tracking servo, head tracking servo in the timing-based servo system will be described. However, the head tracking servo of the invention is not limited to the following specific aspect.

In the head tracking servo in the timing-based servo system (hereinafter, referred to as a “timing-based servo”), a plurality of servo patterns having two or more different shapes are formed in a magnetic layer, and a position of a servo head is recognized by an interval of time in a case where the servo head has read the two servo patterns having different shapes and an interval of time in a case where the servo head has read two servo patterns having the same shapes. The position of the magnetic head of the magnetic tape in the width direction is controlled based on the position of the servo head recognized as described above. In one aspect, the magnetic head, the position of which is controlled here, is a magnetic head (reproducing head) which reproduces information recorded on the magnetic tape, and in another aspect, the magnetic head is a magnetic head (recording head) which records information in the magnetic tape.

FIG. 1 shows an example of disposition of data bands and servo bands. In FIG. 1, a plurality of servo bands 10 are disposed to be interposed between guide bands 12 in a magnetic layer of a magnetic tape 1. A plurality of regions 11 each of which is interposed between two servo bands are data bands. The servo pattern is a magnetized region and is formed by magnetizing a specific region of the magnetic layer by a servo write head. The region magnetized by the servo write head (position where a servo pattern is formed) is determined by standards. For example, in an LTO Ultrium format tape which is based on a local standard, a plurality of servo patterns tilted in a tape width direction as shown in FIG. 2 are formed on a servo band in a case of manufacturing a magnetic tape. Specifically, in FIG. 2, a servo frame SF on the servo band 10 is configured with a servo sub-frame 1 (SSF1) and a servo sub-frame 2 (SSF2). The servo sub-frame 1 is configured with an A burst (in FIG. 2, reference numeral A) and a B burst (in FIG. 2, reference numeral B). The A burst is configured with servo patterns A1 to A5 and the B burst is configured with servo patterns B1 to B5. Meanwhile, the servo sub-frame 2 is configured with a C burst (in FIG. 2, reference numeral C) and a D burst (in FIG. 2, reference numeral D). The C burst is configured with servo patterns C1 to C4 and the D burst is configured with servo patterns D1 to D4. Such 18 servo patterns are disposed in the sub-frames in the arrangement of 5, 5, 4, 4, as the sets of 5 servo patterns and 4 servo patterns, and are used for recognizing the servo frames. FIG. 2 shows one servo frame for explaining. However, in practice, in the magnetic layer of the magnetic tape in which the head tracking servo in the timing-based servo system is performed, a plurality of servo frames are disposed in each servo band in a running direction. In FIG. 2, an arrow shows the running direction. For example, an LTO Ultrium format tape generally includes 5,000 or more servo frames per a tape length of 1 m, in each servo band of the magnetic layer. The servo head sequentially reads the servo patterns in the plurality of servo frames, while coming into contact with and sliding on the surface of the magnetic layer of the magnetic tape transported in the magnetic tape device.

In the head tracking servo in the timing-based servo system, a position of a servo head is recognized based on an interval of time in a case where the servo head has read the two servo patterns (reproduced servo signals) having different shapes and an interval of time in a case where the servo head has read two servo patterns having the same shapes. The time interval is normally obtained as a time interval of a peak of a reproduced waveform of a servo signal. For example, in the aspect shown in FIG. 2, the servo pattern of the A burst and the servo pattern of the C burst are servo patterns having the same shapes, and the servo pattern of the B burst and the servo pattern of the D burst are servo patterns having the same shapes. The servo pattern of the A burst and the servo pattern of the C burst are servo patterns having the shapes different from the shapes of the servo pattern of the B burst and the servo pattern of the D burst. An interval of the time in a case where the two servo patterns having different shapes are read by the servo head is, for example, an interval between the time in a case where any servo pattern of the A burst is read and the time in a case where any servo pattern of the B burst is read. An interval of the time in a case where the two servo patterns having the same shapes are read by the servo head is, for example, an interval between the time in a case where any servo pattern of the A burst is read and the time in a case where any servo pattern of the C burst is read. The head tracking servo in the timing-based servo system is a system supposing that occurrence of a deviation of the time interval is due to a position change of the magnetic tape in the width direction, in a case where the time interval is deviated from the set value. The set value is a time interval in a case where the magnetic tape runs without occurring the position change in the width direction. In the timing-based servo system, the magnetic head is moved in the width direction in accordance with a degree of the deviation of the obtained time interval from the set value. Specifically, as the time interval is greatly deviated from the set value, the magnetic head is greatly moved in the width direction. This point is applied to not only the aspect shown in FIGS. 1 and 2, but also to entire timing-based servo systems.

For the details of the head tracking servo in the timing-based servo system, well-known technologies such as technologies disclosed in U.S. Pat. No. 5,689,384A, U.S. Pat. No. 6,542,325B, and U.S. Pat. No. 7,876,521B can be referred to, for example. In addition, for the details of the head tracking servo in the amplitude-based servo system, well-known technologies disclosed in U.S. Pat. No. 5,426,543A and U.S. Pat. No. 5,898,533A can be referred to, for example.

According to one aspect of the invention, a magnetic tape used in a magnetic tape device in which a TMR head is used as a servo head, the magnetic tape including: a magnetic layer including ferromagnetic powder and a binding agent on a non-magnetic support, in which the magnetic layer includes a servo pattern, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, an XRD intensity ratio is 0.5 to 4.0, and a vertical direction squareness ratio is 0.65 to 1.00, is also provided. The details of the magnetic tape are also as the descriptions regarding the magnetic tape device according to one aspect of the invention.

EXAMPLES

Hereinafter, the invention will be described with reference to examples. However, the invention is not limited to aspects shown in the examples. “Parts” and “%” in the following description mean “parts by mass” and “mass %”, unless otherwise noted. In addition, steps and evaluations described below are performed in an environment of an atmosphere temperature of 23° C.±1° C., unless otherwise noted.

Example 1

1. Manufacturing of Magnetic Tape

A list of components of each layer forming composition is shown below.

List of Components of Magnetic Layer Forming Composition

Magnetic Solution

Plate-shaped ferromagnetic hexagonal ferrite powder (M-type barium ferrite): 100.0 parts

-   -   (Activation volume: 1,500 nm³)

Oleic acid: 2.0 parts

A vinyl chloride copolymer (MR-104 manufactured by Zeon Corporation): 10.0 parts

SO₃Na group-containing polyurethane resin: 4.0 parts

-   -   (Weight-average molecular weight: 70,000, SO₃Na group: 0.07         meq/g)

An amine-based polymer (DISPERBYK-102 manufactured by BYK Additives & Instruments): 6.0 parts

Methyl ethyl ketone: 150.0 parts

Cyclohexanone: 150.0 parts

Abrasive Liquid

α-alumina: 6.0 parts

1 (BET specific surface area: 19 m²/g, Mohs hardness: 9)

SO₃Na group-containing polyurethane resin: 0.6 parts

-   -   (Weight-average molecular weight: 70,000, SO₃Na group: 0.1         meq/g)

2,3-Dihydroxynaphthalene: 0.6 parts

Cyclohexanone: 23.0 parts

Projection Forming Agent Liquid

Colloidal silica: 2.0 parts

-   -   (Average particle size: 80 nm)

Methyl ethyl ketone: 8.0 parts

Lubricant and Curing Agent Liquid

Stearic acid: 3.0 parts

Stearic acid amide: 0.3 parts

Butyl stearate: 6.0 parts

Methyl ethyl ketone: 110.0 parts

Cyclohexanone: 110.0 parts

Polyisocyanate (CORONATE (registered trademark) L manufactured by Nippon Polyurethane Industry Co., Ltd.): 3.0 parts

List of Components of Non-Magnetic Layer Forming Composition

Non-magnetic inorganic powder: α-iron oxide: 100.0 parts

-   -   (Average particle size: 10 nm, BET specific surface area: 75         m²/g)

Carbon black: 25.0 parts

-   -   (Average particle size: 20 nm)

A SO₃Na group-containing polyurethane resin: 18.0 parts

-   -   (Weight-average molecular weight: 70,000, content of SO₃Na         group: 0.2 meq/g)

Stearic acid: 1.0 part

Cyclohexanone: 300.0 parts

Methyl ethyl ketone: 300.0 parts

List of Components of Back Coating Layer Forming Composition

Non-magnetic inorganic powder: α-iron oxide: 80.0 parts

-   -   (Average particle size: 0.15 μm, BET specific surface area: 52         m²/g)

Carbon black: 20.0 parts

-   -   (Average particle size: 20 nm)

A vinyl chloride copolymer: 13.0 parts

A sulfonic acid group-containing polyurethane resin: 6.0 parts

Phenylphosphonic acid: 3.0 parts

Cyclohexanone: 155.0 parts

Methyl ethyl ketone: 155.0 parts

Stearic acid: 3.0 parts

Butyl stearate: 3.0 parts

Polyisocyanate: 5.0 parts

Cyclohexanone: 200.0 parts

Preparation of Magnetic Layer Forming Composition

The magnetic layer forming composition was prepared by the following method.

A dispersion liquid A was prepared by dispersing (first stage) various components of the magnetic solution with a batch type vertical sand mill by using zirconia beads having a bead diameter of 0.5 mm (first dispersion beads, density of 6.0 g/cm³) for 24 hours, and then performing filtering with a filter having a hole diameter of 0.5 μm. The used amount of zirconia beads was 10 times of the amount of the ferromagnetic hexagonal barium ferrite powder based on mass.

After that, a dispersion liquid (dispersion liquid B) was prepared by dispersing (second stage) dispersion liquid A with a batch type vertical sand mill by using diamond beads having a bead diameter shown in Table 1 (second dispersion beads, density of 3.5 g/cm³) for 1 hour, and then separating diamond beads by using a centrifugal separator. The magnetic solution is the dispersion liquid B obtained as described above. The used amount of diamond beads was 10 times of the amount of the ferromagnetic hexagonal barium ferrite powder based on mass.

Regarding the abrasive liquid, various components of the abrasive liquid were mixed with each other and put in a transverse bead mill dispersing device together with zirconia beads having a bead diameter of 0.3 mm, so as to perform the adjustment so that a value of bead volume/(abrasive liquid volume+bead volume) was 80%, the bead mill dispersion process was performed for 120 minutes, the liquid after the process was extracted, and an ultrasonic dispersion filtering process was performed by using a flow type ultrasonic dispersion filtering device. By doing so, the abrasive liquid was prepared.

The magnetic layer forming composition was prepared by introducing the prepared magnetic solution, the abrasive liquid, the projection forming agent liquid, and the lubricant, and the curing agent liquid in a dissolver stirrer, stirring the mixture at a circumferential speed of 10 m/sec for 30 minutes, and performing a process of 3 passes at a flow rate of 7.5 kg/min with a flow type ultrasonic dispersing device, and filtering the mixture with a filter having a hole diameter of 1 μm.

Preparation of Non-Magnetic Layer Forming Composition

A non-magnetic layer forming composition was prepared by dispersing various components of the non-magnetic layer forming composition with a batch type vertical sand mill by using zirconia beads having a bead diameter of 0.1 mm for 24 hours, and then performing filtering with a filter having a hole diameter of 0.5 μm.

Preparation of Back Coating Layer Forming Composition

Components among various components of the back coating layer forming composition except a lubricant (stearic acid and butyl stearate), polyisocyanate, and 200.0 parts of cyclohexanone were kneaded and diluted by an open kneader, and subjected to a dispersion process of 12 passes, with a transverse beads mill dispersing device and zirconia beads having a bead diameter of 1 mm, by setting a bead filling percentage as 80 volume %, a circumferential speed of rotor distal end as 10 m/sec, and a retention time for 1 pass as 2 minutes. After that, the remaining components were added and stirred with a dissolver, the obtained dispersion liquid was filtered with a filter having a hole diameter of 1 μm and a back coating layer forming composition was prepared.

Manufacturing Method of Magnetic Tape

The non-magnetic layer forming composition prepared as described above was applied to a surface of a support made of polyethylene naphthalate having a thickness of 5.00 μm so that the thickness after the drying becomes 1.00 μm and was dried to form a non-magnetic layer. The magnetic layer forming composition prepared as described above was applied onto the surface of the formed non-magnetic layer so that the thickness after the drying becomes 70 nm (0.07 μm) and a coating layer was formed. A homeotropic alignment process was performed by applying a magnetic field having a strength shown in Table 1 in a vertical direction with respect to the surface of the coating layer, while the coating layer of the magnetic layer forming composition is wet (not dried). After that, the coating layer was dried to form a magnetic layer.

After that, the back coating layer forming composition prepared as described above was applied to the surface of the support on a side opposite to the surface where the non-magnetic layer and the magnetic layer are formed, so that the thickness after the drying becomes 0.40 μm, and was dried.

A calender process (surface smoothing treatment) was performed with respect to the magnetic tape obtained as described above by a calender configured of only a metal roll, at a speed of 100 m/min, linear pressure of 300 kg/cm (294 kN/m), and a surface temperature of a calender roll of 90° C., and then, a thermal treatment was performed in the environment of the atmosphere temperature of 70° C. for 36 hours. After the thermal treatment, the slitting was performed to have a width of ½ inches (0.0127 meters), and a magnetic tape is obtained.

By doing so, a magnetic tape for forming a servo pattern in the magnetic layer was manufactured.

In a state where the magnetic layer of the manufactured magnetic tape was demagnetized, servo patterns having disposition and shapes according to the LTO Ultrium format were formed on the magnetic layer by using a servo write head mounted on a servo tester. Accordingly, a magnetic tape including data bands, servo bands, and guide bands in the disposition according to the LTO Ultrium format in the magnetic layer, and including servo patterns having the disposition and the shape according to the LTO Ultrium format on the servo band is manufactured. The servo tester includes a servo write head and a servo head. This servo tester was also used in evaluations which will be described later.

The thickness of each layer and the thickness of the non-magnetic support of the manufactured magnetic tape were acquired by the following method, and it was confirmed that the thicknesses obtained are the thicknesses described above.

A cross section of the magnetic tape in a thickness direction was exposed to ion beams and the exposed cross section was observed with a scanning electron microscope. Various thicknesses were obtained as an arithmetical mean of thicknesses obtained at two portions in the thickness direction in the cross section observation.

A part of the magnetic tape manufactured by the method described above was used in the evaluation of physical properties described below, and the other part was used in order to measure an SNR which will be described later.

The activation volume of the ferromagnetic hexagonal ferrite powder described above is a value calculated by performing measurement by using a powder lot which is the same as that of ferromagnetic hexagonal ferrite powder used in the magnetic layer forming composition. The magnetic field sweep rates in the coercivity Hc measurement part at timing points of 3 minutes and 30 minutes were measured by using an oscillation sample type magnetic-flux meter (manufactured by Toei Industry Co., Ltd.), and the activation volume was calculated from the relational expression described above. The measurement was performed in the environment of 23° C.±1° C.

2. Evaluation of Physical Properties of Magnetic Tape

(1) XRD Intensity Ratio

A tape sample was cut out from the manufactured magnetic tape.

Regarding the cut-out tape sample, the surface of the magnetic layer was irradiated with X-ray by using a thin film X-ray diffraction device (Smart Lab manufactured by Rigaku Corporation), and the In-Plane XRD was performed by the method described above.

The peak intensity Int(114) of the diffraction peak of the (114) plane and the peak intensity Int(110) of the diffraction peak of a (110) plane of a hexagonal ferrite crystal structure were obtained from the X-ray diffraction spectra obtained by the In-Plane XRD, and the XRD intensity ratio (Int(110)/Int(114)) was calculated.

(2) Vertical Direction Squareness Ratio

A vertical direction squareness ratio of the manufactured magnetic tape was obtained by the method described above using an oscillation sample type magnetic-flux meter (manufactured by Toei Industry Co., Ltd.).

(3) Center Line Average Surface Roughness Ra Measured Regarding Surface of Magnetic Layer

The measurement regarding a measurement area of 40 μm×40 μm in the surface of the magnetic layer of the magnetic tape was performed with an atomic force microscope (AFM, Nanoscope 4 manufactured by Veeco Instruments, Inc.) in a tapping mode, and a center line average surface roughness Ra was acquired. RTESP-300 manufactured by BRUKER is used as a probe, a scan speed (probe movement speed) was set as 40 μm/sec, and a resolution was set as 512 pixel×512 pixel.

3. Measurement of SNR

In an environment of an atmosphere temperature of 23° C.±1° C. and relative humidity of 50%, the servo head of the servo tester was replaced with a commercially available TMR head (element width of 70 nm) as a reproducing head for HDD. The reading of a servo pattern was performed by attaching the magnetic tape manufactured in the section 1. to the servo tester, and the SNR was obtained as a ratio of the output and noise. The SNR was calculated as a relative value by setting the SNR measured as 0 dB in Comparative Example 1 which will be described later. In a case where the SNR calculated as described above is equal to or greater than 2.0 dB, it is possible to evaluate that performance of dealing with future needs accompanied with high-density recording is obtained.

Examples 2 to 5 and Comparative Examples 1 to 11

1. Manufacturing of Magnetic Tape

A magnetic tape was manufactured in the same manner as in Example 1, except that various conditions shown in Table 1 were changed as shown in Table 1.

In Table 1, in the comparative examples in which “none” is shown in a column of the dispersion beads and a column of the time, the magnetic layer forming composition was prepared without performing the second stage in the magnetic solution dispersion process.

In Table 1, in the comparative examples in which “none” is shown in a column of the homeotropic alignment process magnetic field intensity, the magnetic layer was formed without performing the orientation process.

2. Evaluation of Physical Properties of Magnetic Tape

Various physical properties of the manufactured magnetic tape were evaluated in the same manner as in Example 1.

3. Measurement of SNR

The SNR was measured by the same method as that in Example 1, by using the manufactured magnetic tape. In Examples 2 to 5 and Comparative Examples 2 to 6, the TMR head which was the same as that in Example 1 was used as a servo head. In Comparative Examples 1 and 7 to 11, a commercially available spin valve type GMR head (element width of 70 nm) was used as a servo head.

The results of the evaluations described above are shown in Table 1.

TABLE 1 Magnetic solution dispersion process second stage Dispersion beads Used amount (mass of beads with respect to mass of Homeotropic Magnetic layer ferromagnetic alignment process center line average Bead hexagonal ferrite magnetic field surface roughness Kind diameter powder) Time intensity Ra Comparative Example 1 None None None None None 2.0 nm Comparative Example 2 None None None None None 2.0 nm Comparative Example 3 None None None None 0.15 T 2.0 nm Comparative Example 4 None None None None 0.30 T 2.0 nm Comparative Example 5 Diamond 500 nm 10 times 1 h 1.00 T 2.0 nm Comparative Example 6 Diamond 500 nm 10 times 1 h None 2.0 nm Comparative Example 7 Diamond 500 nm 10 times 1 h 0.15 T 2.0 nm Comparative Example 8 Diamond 500 nm 10 times 1 h 0.20 T 2.0 nm Comparative Example 9 Diamond 500 nm 10 times 1 h 0.30 T 2.0 nm Comparative Example 10 Diamond 500 nm 10 times 1 h 0.50 T 2.0 nm Comparative Example 11 Diamond 500 nm 20 times 1 h 0.15 T 2.0 nm Example 1 Diamond 500 nm 10 times 1 h 0.15 T 2.0 nm Example 2 Diamond 500 nm 10 times 1 h 0.20 T 2.0 nm Example 3 Diamond 500 nm 10 times 1 h 0.30 T 2.0 nm Example 4 Diamond 500 nm 10 times 1 h 0.50 T 2.0 nm Example 5 Diamond 500 nm 20 times 1 h 0.15 T 2.0 nm Vertical XRD intensity ratio direction Int(110)/Int(114) squareness ratio Servo head SNR (dB) Comparative Example 1 0.2 0.55 GMR 0 Comparative Example 2 0.2 0.55 TMR 1.0 Comparative Example 3 3.8 0.63 TMR 1.4 Comparative Example 4 5.0 0.75 TMR 1.3 Comparative Example 5 6.1 0.90 TMR 1.3 Comparative Example 6 0.3 0.66 TMR 1.1 Comparative Example 7 0.5 0.70 GMR 0.5 Comparative Example 8 1.5 0.75 GMR 0.6 Comparative Example 9 2.3 0.80 GMR 0.7 Comparative Example 10 4.0 0.85 GMR 0.8 Comparative Example 11 0.7 0.83 GMR 0.7 Example 1 0.5 0.70 TMR 2.5 Example 2 1.5 0.75 TMR 2.7 Example 3 2.3 0.80 TMR 3.0 Example 4 4.0 0.85 TMR 2.8 Example 5 0.7 0.83 TMR 2.7

As shown in Table 1, in Examples 1 to 5, the servo pattern could be read at a high SNR by using the TMR head as the servo head, compared to Comparative Examples 1 to 11.

The invention is effective for usage of magnetic recording for which high-sensitivity reproducing of information recorded with high density is desired. 

What is claimed is:
 1. A magnetic tape device comprising: a magnetic tape; and a servo head, wherein the servo head is a magnetic head including a tunnel magnetoresistance effect type element as a servo pattern reading element, the magnetic tape includes a non-magnetic support, and a magnetic layer including ferromagnetic powder and a binding agent on the non-magnetic support, the magnetic layer includes a servo pattern, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, an intensity ratio Int(110)/Int(114) of a peak intensity Int(110) of a diffraction peak of a (110) plane with respect to a peak intensity Int(114) of a diffraction peak of a (114) plane of a hexagonal ferrite crystal structure obtained by an X-ray diffraction analysis of the magnetic layer by using an In-Plane method is 0.5 to 4.0, and a vertical direction squareness ratio of the magnetic tape is 0.65 to 1.00.
 2. The magnetic tape device according to claim 1, wherein the vertical direction squareness ratio of the magnetic tape is 0.65 to 0.90.
 3. The magnetic tape device according to claim 1, wherein a center line average surface roughness Ra measured regarding a surface of the magnetic layer is equal to or smaller than 2.5 nm.
 4. The magnetic tape device according to claim 1, wherein the magnetic tape includes a non-magnetic layer including non-magnetic powder and a binding agent between the non-magnetic support and the magnetic layer.
 5. A head tracking servo method comprising: reading a servo pattern of a magnetic layer of a magnetic tape by a servo head in a magnetic tape device, wherein the servo head is a magnetic head including a tunnel magnetoresistance effect type element as a servo pattern reading element, the magnetic tape includes a non-magnetic support, and a magnetic layer including ferromagnetic powder and a binding agent on the non-magnetic support, the magnetic layer includes the servo pattern, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, an intensity ratio Int(110)/Int(114) of a peak intensity Int(110) of a diffraction peak of a (110) plane with respect to a peak intensity Int(114) of a diffraction peak of a (114) plane of a hexagonal ferrite crystal structure obtained by an X-ray diffraction analysis of the magnetic layer by using an In-Plane method is 0.5 to 4.0, and a vertical direction squareness ratio of the magnetic tape is 0.65 to 1.00.
 6. The head tracking servo method according to claim 5, wherein the vertical direction squareness ratio of the magnetic tape is 0.65 to 0.90.
 7. The head tracking servo method according to claim 5, wherein a center line average surface roughness Ra measured regarding a surface of the magnetic layer is equal to or smaller than 2.5 nm.
 8. The head tracking servo method according to claim 5, wherein the magnetic tape includes a non-magnetic layer including non-magnetic powder and a binding agent between the non-magnetic support and the magnetic layer. 